PP(Polypropylene Homopolymer) data sheet
--------------------------------------------------------------------------------
LEGEND
A = amorphous - Cr = crystalline - C = clear - E = excellent - G = good - P =
O = opaque - T = translucent- R = Rockwell - S = Shore
--------------------------------------------------------------------------------
STRUCTURE: Cr
SPECIFIC DENSITY: 0.90
WATER ABSORBTION RATE (%): 0.01
ELONGATION (%): 200
TENSILE STRENGTH (psi): 4500
COMPRESSION STRENGTH (psi): 6500
FLEXURAL STRENGTH (psi): 7000
FLEXURAL MODULUS (psi): 190000
IMPACT (IZOD ft. lbs/in): 1
HARDNESS: R95
FABRICATION
- BONDING: P
- ULTRASONIC WELDING: P
- MACHINING: G
DEFLECTION TEMPERATURE (deg. F)
- @ 66 psi: 210
- @ 264 psi: 140
UTILZATION TEMPERATURE (deg. F)
- min: -15
- max: 265
MELTING POINT (deg. F): 338
COEFFICIENT OF EXPANSION: 0.00006
ARC RESISTANCE: 180
DIELECTRIC STRENGTH (kV/mm): 23
TRANSPARENCY: T
UV RESISTANCE: P
CHEMICAL RESISTANCE
- ACIDS:
- ALKALIS:
- SOLVENTS:
|